Our
product range
Quality 1.3813
General Product Description
Material number 1.3813
Short name according to EN 1.3813
Applicable standards WK, TLV 9384 01
Treatment hot-cold solidified
Variations
| Quality | Treatment | Shape | Dimension (mm) |
|---|---|---|---|
| 1.3813 | hot-cold solidified |  Round | 20 - 48 |
Description
The material 1.3813 belongs to the amagnetic steels. Application: Connecting parts, mechanical engineering, mechanically and thermally highly stressed components in shipbuilding, mechanical engineering and vehicle construction as well as in electrical engineering.
Chemical composition (in %)
| C | Cr | Mn | P | S | Si | N | |
|---|---|---|---|---|---|---|---|
| Min | 0,30 | 3,0 | 18,0 | - | - | - | 0,080 |
| Max | 0,50 | 5,0 | 20,0 | 0,050 | 0,015 | 0,50 | 0,12 |
| Element | Min | Max |
|---|---|---|
| C | 0,30 | 0,50 |
| Cr | 3,0 | 5,0 |
| Mn | 18,0 | 20,0 |
| P | - | 0,050 |
| S | - | 0,015 |
| Si | - | 0,50 |
| N | 0,080 | 0,12 |
Mechanical properties (solution annealed / warm-cold worked)
0.2% proof stress Rp0.2 ≥ 500 N/mm2
Elongation at break A5 ≥ 20 %
Notched impact energy (ISO-V) ≥ 90 (Mittelwert aus 3 Proben) J
Hardness 260 – 360 HB
Magnetizability No
Typical areas of application
connectors
electrical engineering
Mechanical engineering
Safety technology
Shipbuilding and vehicle manufacturing
Crushing and wear applications
General properties (solution annealed / warm-cold worked)
Corrosion Resistance
Weldability
Forgeability
Tensionability
Note
All information in this data sheet has been compiled to the best of our knowledge and belief. It is for information purposes only and does not constitute a assured property or guarantee. For the suitability of the material in specific applications, we recommend carrying out appropriate inspections and tests. Any liability for damage or errors is excluded.